Effect of pH on the solubility and volumetric change of ready-to-use Bio-C Repair bioceramic material.

Acidic pH can modify the properties of repair cements. In this study, volumetric change and solubility of the ready-to-use bioceramic repair cement Bio-C Repair (BCR, Angelus, Londrina, PR, Brazil) were evaluated after immersion in phosphate-buffered saline (PBS) (pH 7.0) or butyric acid (pH 4.5). Solubility was determined by the difference in initial and final mass using polyethylene tubes measuring 4 mm high and 6.70 mm in internal diameter that were filled with BCR and immersed in 7.5 mL of PBS or butyric acid for 7 days. The volumetric change was established by using bovine dentin tubes measuring 4 mm long with an internal diameter of 1.5 mm. The dentin tubes were filled with BCR at 37°C for 24 hours. Scanning was performed with micro-computed tomography (micro-CT; SkyScan 1176, Bruker, Kontich, Belgium) with a voxel size of 8.74 µm. Then, the specimens were immersed in 1.5 mL of PBS or butyric acid at and 37 °C for 7 days. After this period, a new micro-CT scan was performed. Bio-C Repair showed greater mass loss after immersion in butyric acid when compared with immersion in PBS (p<0.05). Bio-C Repair showed volumetric loss after immersion in butyric acid and increase in volume after immersion in PBS (p<0.05). The acidic pH influenced the solubility and dimensional stability of the Bio-C Repair bioceramic cement, promoting a higher percentage of solubility and decrease in volumetric values.

Biocompatibility and bioactive potential of NeoPUTTY calcium silicate-based cement: An in vivo study in rats.

AIM: To evaluate the inflammatory reaction and the ability to induce mineralization activity of a new repair material, NeoPUTTY (NPutty; NuSmile, USA), in comparison with Bio-C Repair (BC; Angelus, Brazil) and MTA Repair HP (MTA HP; Angelus, Brazil). METHODOLOGY: Polyethylene tubes were filled with materials or kept empty (control group, CG) and implanted in subcutaneous tissue of rats for 7, 15, 30, and 60 days (n = 6/group). Capsule thickness, number of inflammatory cells (ICs), fibroblasts, collagen content, and von Kossa analysis were performed. Unstained sections were evaluated under polarized light and by immunohistochemistry for osteocalcin (OCN). Data were submitted to two-way anova followed by Tukey's test (p ≤ .05), except for OCN. OCN data were submitted to Kruskal-Wallis and Dunn and Friedman post hoc tests followed by the Nemenyi test at a significance level of 5%. RESULTS: At 7, 15, and 30 days, thick capsules containing numerous ICs were seen around the materials. At 60 days, a moderate inflammatory reaction was observed for NPutty, BC while MTA HP presented thin capsules with moderate inflammatory cells. In all periods, NPutty specimens contained the highest values of ICs (p < .05). From 7 to 60 days, the number of ICs reduced significantly while an increase in the number of fibroblasts and birefringent collagen content was observed. At 7 and 15 days, no significant difference was observed in the immunoexpression of OCN (p > .05). At 30 and 60 days, NPutty showed the lowest values of OCN (p < .05). At 60 days, a similar immunoexpression was observed for BC and MTA HP (p > .05). In all time intervals, capsules around NPutty, BC, and MTA HP showed von Kossa-positive and birefringent structures. CONCLUSIONS: Despite the greater inflammatory reaction promoted by NeoPutty than BC and MTA HP, the reduction in the thickness of capsules, the increase in the number of fibroblasts, and the reduction in the number of ICs indicate that this bioceramic material is biocompatible Furthermore, NeoPutty presents the ability to induce mineralization activity.

Bioactive potential of Bio-C Temp demonstrated by systemic mineralization markers and immunoexpression of bone proteins in the rat connective tissue.

Intracanal medications are used in endodontic treatment due to their antibacterial activity and ability to induce the periapical repair. Among the intracanal medications, the Calen (CAL; SS. White, Brazil) is a calcium hydroxide-based medication that provides an alkaline pH and releases calcium, exerting an antimicrobial activity. Bio-C Temp (BIO; Angelus, Brazil), a ready-to-use bioceramic intracanal medication, was designed to stimulate the mineralized tissues formation. Here, we investigated the bioactive potential of BIO in comparison to the CAL in the rat subcutaneous. Polyethylene tubes filled with medications, and empty tubes (control group, CG) were implanted in the subcutaneous tissue of rats. After 7, 15, 30 and 60 days, the blood was collected for calcium (Ca+2) and alkaline phosphatase (ALP) measurement, and the capsules around the implants were processed for morphological analyses. The data were submitted to two-way ANOVA and Tukey test (p < 0.05). At 7, 15 and 30 days, the ALP level was grater in BIO and CAL than in CG (p < 0.0001). At 7 and 15 days, greater Ca+2 level was seen in the serum of CAL samples. From 7 to 60 days, an increase in the number of fibroblasts, osteocalcin- and osteopontin-immunolabelled cells was observed in BIO and CAL groups (p < 0.0001). In all periods, BIO and CAL specimens showed von Kossa-positive structures. Moreover, ultrastructural analysis revealed globules of mineralization in the capsules around the BIO and CAL specimens. Thus Bio-C Temp caused an increase in the ALP, osteocalcin and osteopontin, which may have allowed the formation of calcite, suggesting bioactive potential.

Flatsonic Ultrasonic Tip Optimizes the Removal of Remaining Filling Material in Flattened Root Canals: A Micro-computed Tomographic Analysis.

INTRODUCTION: The aim of this study was to evaluate the effectiveness of the XP-endo Finisher R (XPFR; FKG Dentaire, La Chaux-de-Fonds, Switzerland) or the Flatsonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, SP, Brazil) in removing remaining filling material after the retreatment of flattened root canals using micro-computed tomographic imaging. METHODS: Twenty-four flattened distal root canals of mandibular molars with a buccolingual diameter 4 or more times larger than the mesiodistal diameter were prepared with Reciproc Blue (RB) R40 (VDW GmbH, Munich, Germany) and filled using the Tagger hybrid technique. All canals were retreated with RB R40, and apical enlargement was performed with RB R50 (VDW GmbH). The specimens were randomly distributed into 2 groups: XPFR or Flatsonic (n = 12). The percentage of remaining filling material after retreatment and centralization ability was evaluated. Data were submitted to Mann-Whitney, Wilcoxon, and unpaired t tests (α = 5%). RESULTS: Greater capacity to remove remaining filling material in the entire canal and the cervical and middle thirds was observed for the Flatsonic compared with the XPFR (P < .05). However, both supplementary cleaning techniques showed a similar percentage of residual filling material in the apical third (P > .05). No difference was observed in the centralization ability between the techniques (P > .05). CONCLUSIONS: The Flatsonic promotes greater removal of remaining filling material than the XPFR in the retreatment of flattened root canals. However, both supplementary cleaning approaches were similar in the apical third. The XPFR and Flatsonic were able to maintain root canal centralization.

Diamond-coated ultrasonic tip decreases debris and uninstrumented surface after preparation of curved canals with isthmus.

The aim of this study was to evaluate root canal preparation with nickel titanium rotary instruments and complementary preparation with ultrasonic tip in curved canals of mandibular molars with isthmus. Twenty-eight mesial roots of mandibular molars with curvature between 20° and 40° and presence of isthmus throughout the entire extension of the root canals were prepared using ProDesign Logic CM (PDL) up to size 40.05, or HyFlex EDM (HFEDM) up to size 40.04. Complementary preparation was performed in the isthmus region using the ultrasonic insert E18D (Helse, Istmo Diamantada). The root canals were scanned using micro-CT (SkyScan 1176) at 9 µm voxel size before and after each preparation step. Transportation, percentage of increase in volume, debris and uninstrumented surface (UNS) were evaluated. Mann Whitney, Wilcoxon, paired and non-paired t-tests were used for statistical analysis (α = 0.05). The canals prepared with PDL and HFEDM obtained similar results for all the variables assessed before using E18D (p > 0.05). E18D significantly decreased the percentage of debris and UNS values in both Groups (p < 0.05). The complementary preparations with E18D caused a smaller quantity of debris in the isthmus of the canals previously prepared with PDL in comparison with HFEDM (p < 0.05). PDL and HFEDM provided similar root canal preparation. PDL promoted a smaller quantity of Debris in the isthmus than HFEDM after using E18D. E18D significantly improved cleaning, and reduced Debris and UNS.

Continuous Wave of Condensation Improves the Filling of Curved Canals: a Micro-CT Study / La condensación de onda contínua mejora el selle de canales curvos: un estudio de micro-CT

Abstract The aim of this study was to compare the filling capacity in curved root canal using a new continuous wave of condensation technique (Termo Pack II, Easy Dental Equipments, Brazil) or lateral compaction. The percentage of voids in the filling of mesial root canals of mandibular molars was assessed by micro-computed tomography (micro-CT). Mesial root canals (n=24) of mandibular molars with a degree of curvature between 20° and 40° were prepared using rotary system (ProDesign Logic, Easy, Brazil) up to #35, .05 taper. The root canals were filled by using the continuous wave of condensation system or lateral compaction and AH Plus sealer (n=12). Scanning at 9 µm was performed after preparation and after filling by using micro-CT SkyScan 1176. The volumetric percentage of filling material and voids (total length and in each root canal third) were calculated. Data were analyzed using ANOVA/ Tukey and Student's t tests (α=0.05). Before the filling techniques, the root canals volume after preparation was similar (p>0.05). The root canals filled by the continuous wave of condensation technique presented the lowest percentage of voids, and the greatest percentage of filling material in total length and thirds (cervical, middle and apical) (p<0.05). Both techniques were not able of completely filling the root canals. The continuous wave of condensation technique Termo Pack II promoted better root canal filling in curved root canals, when compared with lateral compaction.

Resumen El objetivo de este estudio fue comparar la capacidad de obturación en conductos radiculares curvos utilizando una nueva técnica de condensación de onda continua (Termo Pack II, Easy Dental Equipments, Brasil) vs compactación lateral. El porcentaje de brechas en la obturación de los conductos radiculares mesiales de los molares mandibulares se evaluó mediante microtomografía computarizada (micro-CT). Se prepararon conductos radiculares mesiales (n=24) de molares mandibulares con un grado de curvatura entre 20° y 40° utilizando un sistema rotatorio (ProDesign Logic, Easy, Brasil) al #35, conicidad 0,05. Los conductos radiculares se obturaron utilizando un sistema de condensación de onda contínua o compactación lateral y cemento AH Plus (n=12). Se realizó un escaneo de 9 µm después de la preparación y después de la obturación usando el micro-CT SkyScan 1176. Se calculó el porcentaje volumétrico de material de obturación y vacíos (longitud total y en cada tercio del conducto radicular). Los datos se analizaron utilizando las pruebas ANOVA/Tukey y t de Student (α=0,05). Antes de las técnicas de obturación, el volumen de los conductos radiculares después de la preparación fue similar (p>0,05). Los conductos radiculares obturados con la técnica de condensación por onda contínua presentaron el menor porcentaje de vacíos y el mayor porcentaje de material de obturación en longitud total y en tercios (cervical, medio y apical) (p<0,05). Ambas técnicas no fueron capaces de llenar completamente los conductos radiculares. La técnica de condensación de onda contínua Termo Pack II promovió un mejor relleno del conducto radicular en conductos radiculares curvos en comparación con la compactación lateral.

Effect of Endo-Z bur or Bladesonic ultrasonic tip on the adaptation of filling material. A micro-CT study.

This study aimed to evaluate the effect of apicoectomy performed with a bur or an ultrasonic tip on the adaptation of the filling material to root canal dentin. Twenty human mandibular incisors were selected and prepared with a ProDesign Logic system up to diameter 40/.05. The root canals were filled with Bio-C Sealer (Angelus, PR, Brazil) using the single cone technique and were stored at 37ºC and 95% relative humidity for 7 days. After this period, the apicoectomy of the 3 millimeters of the root apex was performed using Endo-Z bur (Dentsply Sirona) or Bladesonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, Brazil) (n=10). The specimens were scanned by micro-computed tomography (micro-CT; SkyScan 1176) with a voxel size of 8.74 µm after obturation and after apicoectomy. The percentage of voids at the interface between the filling material and the root canal wall was evaluated in the apical 4 mm of the root after apicoectomy, besides the time cutting to both devices. The data obtained were submitted to paired and unpaired t-tests (α = 0.05). Endo-Z and Bladesonic increased the percentage of voids between the filling material and the dentin after apicectomy (p<0.05), and they were similar (p>0.05). Endo-Z has a shorter time to perform apicoectomy compared to Bladesonic (p<0.05). Apicectomies with Endo-Z or Bladesonic could harm the material/dentin interface, while the Endo-Z bur was faster than the Bladesonic ultrasonic tip.

Effect of radiopacifier and liquid in the physicochemical and biological properties of calcium silicate clinker Angelus: A laboratory investigation.

The aim of this study was to evaluate the effect of radiopacifier calcium tungstate and manipulation with distilled water (DW) or liquid with additives (LA) on calcium silicate clinker Angelus (CL) properties, compared with MTA (Angelus, Brazil) and MTA Repair HP (MTAHP, Angelus, Brazil). The physicochemical properties, cellular viability and bioactivity were evaluated. ANOVA/Tukey and Bonferroni tests were performed (α = 0.05). There was no difference in material setting time (p > 0.05). MTA and MTAHP were similar (p > 0.05) and had greater radiopacity than CL + DW and CL + LA (p < 0.05). All experimental materials showed mass increase, alkalinisation capacity, besides biocompatibility and bioactivity at 3 and 7 days. The different liquids had no influence in the biological properties and bioactivity of the calcium silicate clinker Angelus. Calcium tungstate provided radiopacity, without changing the setting time, maintaining the mass increase and alkalinisation ability of the calcium silicate materials.

Effect of Endo-Z bur or Bladesonic ultrasonic tip on the adaptation of filling material. A micro-CT study

Abstract This study aimed to evaluate the effect of apicoectomy performed with a bur or an ultrasonic tip on the adaptation of the filling material to root canal dentin. Twenty human mandibular incisors were selected and prepared with a ProDesign Logic system up to diameter 40/.05. The root canals were filled with Bio-C Sealer (Angelus, PR, Brazil) using the single cone technique and were stored at 37ºC and 95% relative humidity for 7 days. After this period, the apicoectomy of the 3 millimeters of the root apex was performed using Endo-Z bur (Dentsply Sirona) or Bladesonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, Brazil) (n=10). The specimens were scanned by micro-computed tomography (micro-CT; SkyScan 1176) with a voxel size of 8.74 µm after obturation and after apicoectomy. The percentage of voids at the interface between the filling material and the root canal wall was evaluated in the apical 4 mm of the root after apicoectomy, besides the time cutting to both devices. The data obtained were submitted to paired and unpaired t-tests (α = 0.05). Endo-Z and Bladesonic increased the percentage of voids between the filling material and the dentin after apicectomy (p<0.05), and they were similar (p>0.05). Endo-Z has a shorter time to perform apicoectomy compared to Bladesonic (p<0.05). Apicectomies with Endo-Z or Bladesonic could harm the material/dentin interface, while the Endo-Z bur was faster than the Bladesonic ultrasonic tip.

Resumo O objetivo deste estudo foi avaliar o efeito da apicectomia realizada com broca ou inserto ultrassônico na adaptação do material obturador á dentina do canal radicular. Vinte incisivos inferiores humanos extraídos foram selecionados e preparados com o sistema ProDesign Logic até o diâmetro 40/.05. Os canais radiculares foram obturados com Bio-C Sealer (Angelus, PR, Brasil) por meio da técnica de cone único e foram armazenados em estufa a 37ºC e umidade relativa de 95% por 7 dias. Após esse período, foi realizada apicectomia dos 3 milímetros apicais utilizando broca Endo-Z (Maillefer - Dentsply) ou inserto ultrassônico BladeSonic (Helse Ultrasonic, Santa Rosa de Viterbo, Brasil) (n=10). Os espécimes foram escaneados por meio de microtomografia computadorizada (micro-CT; SkyScan 1176) com tamanho de voxel de 8,74 µm após obturação e após apicectomia. Please, correct this sentece to O percentual de falhas na interface entre o material obturador e a parede dentinaria foi avaliado nos 4 mm apicais da raiz apos apicectomia, alem do tempo de corte para ambos dispositivos. Os dados obtidos foram submetidos aos testes t pareado e não pareado (α = 0,05). Endo-Z e Bladesonic aumentaram o percentual de vazios entre o material obturador e a parede da dentina após apicectomia (p<0.05), sendo semelhantes entre si (p>0.05). Endo-Z demonstrou menor tempo para realizar apicectomia em comparação com Bladesonic (p<0.05). Apicectomias com Endo-Z ou Bladesonic podem prejudicar a interface material obturador/dentina, sendo a broca Endo-Z mais rápida que a ponta ultrassônica Bladesonic.

Effect of voxel size of Micro-CT on the assessment of root canal preparation

The aim of this study was to assess the influence of micro-computed tomography (micro-CT) voxel size on evaluation of root canal preparation using rotary heat-treated nickel-titanium files. Curved mesial root canals of mandibular molars were prepared using ProDesign Logic 30/.05 (PDL) or HyFlex EDM 25/.08 (HEDM) (n=12). The specimens were scanned using micro-CT with 5μm of voxel size before and after root canal preparation. Images with sub-resolution of 10 and 20μm voxel sizes were obtained. The percentage of volume increase, debris and uninstrumented root canal surface were analyzed in the different voxel sizes. Data were compared using unpaired Student's t-test and ANOVA statistical tests (α=0.05). No differences were observed for percentage of volume increase, debris and instrumented surface between the root canals prepared by PDL and HEDM (p>0.05). Both systems promoted higher percentage of debris in the apical third compared to the middle third (p0.05). PDL and HEDM had similar root canal preparation capacity. Micro-CT images using different voxel sizes did not influence the results of volume increase and debris evaluation. However, images at 5µm showed greater accuracy to evaluate the percentage of uninstrumented surfaces.

El objetivo de este estudio fue evaluar la influencia del tamaño de vóxel de la microtomografía computarizada (micro-CT) en la evaluación de la preparación del conducto radicular utilizando limas rotatorias de níquel-titanio tratadas térmicamente. Se prepararon conductos radiculares mesiales curvos de molares mandibulares usando ProDesign Logic 30/.05 (PDL) o HyFlex EDM 25/.08 (HEDM) (n=12). Las muestras se escanearon usando micro-CT con un tamaño de vóxel de 5μm antes y después de la preparación del conducto radicular. Se obtuvieron imágenes con subresolución de vóxeles de 10 y 20μm. Se analizó el porcentaje de aumento de volumen, residuos y superficie del conducto radicular no instrumentado en diferentes tamaños de vóxel. Los datos se compararon usando la prueba t de Student no pareada y las pruebas estadísticas ANOVA (α=0,05). No se observaron diferencias en el porcentaje de aumento de volumen, detritus y superficie instrumentada entre los conductos radiculares preparados por PDL y HEDM (p>0,05). Ambos sistemas promovieron un mayor porcentaje de detritos en el tercio apical en comparación con el tercio medio (p0,05). PDL y HEDM tenían una capacidad de preparación del conducto radicular similar. Las imágenes de micro-CT que utilizan diferentes tamaños de vóxel no influyeron en los resultados de la evaluación del volumen y los desechos. Sin embargo, las imágenes de 5µm mostraron una mayor precisión al evaluar el porcentaje de superficies no instrumentadas.

Biocompatibility, bioactive potential, porosity, and interface analysis calcium silicate repair cements in a dentin tube model.

OBJECTIVES: This study is to evaluate biocompatibility, bioactive potential, porosity, and dentin/material interface of Bio-C Repair (BIOC-R), MTA Repair HP (MTAHP), and Intermediate Restorative Material (IRM). MATERIALS AND METHODS: Dentin tubes were implanted into subcutaneous of rats for 7, 15, 30, and 60 days. Thickness of capsules, number of inflammatory cells (ICs), interleukin-6 (IL-6), osteocalcin (OCN), and von Kossa were evaluated. Porosity and material/dentin interface voids were also analyzed. Data were submitted to ANOVA and Tukey's tests (p < 0.05). RESULTS: IRM capsules were thicker and contained greater ICs and IL-6-immunopositive cells at 7 and 15 days. BIOC-R capsules exhibited higher thickness and ICs at 7 days and greater IL-6 at 7 and 15 days than MTAHP (p < 0.05). At 30 and 60 days, no significant difference was observed among the groups. OCN-immunopositive cells, von Kossa-positive, and birefringent structures were observed in BIOC-R and MTAHP. MTAHP exhibited higher porosity and interface voids (p < 0.05). CONCLUSIONS: BIOC-R, MTAHP, and IRM are biocompatible. Bioceramics materials demonstrate bioactive potential. MTAHP presented the highest porosity and presence of voids. CLINICAL RELEVANCE: BIOC-R and MTAHP have adequate biological properties. BIOC-R demonstrated lower porosity and presence of voids, which may represent better sealing for its clinical applications.

Physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic repair material.

The aim of this study was to evaluate the physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic material, Bio-C Repair (Angelus), in comparison with White MTA (Angelus) and Biodentine (Septodont). The physicochemical properties of setting time, radiopacity, pH, solubility, dimensional and volumetric changes were evaluated. Biocompatibility and bioactivity were assessed in Saos-2 osteoblast cell cultures by the MTT assay 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), Alizarin Red (ARS), and cell migration tests. Statistical analysis was performed by ANOVA, Tukey or Bonferroni tests (α = 0.05). Bio-C Repair had the longest setting time (p < 0.05), but radiopacity and solubility were accordance with the ISO 6876/2012 standards, besides linear expansion. Bio-C Repair and MTA had similar volumetric change (p > 0.05); lower than Biodentine (p < 0.05). All the materials evaluated had an alkaline pH. Bio-C Repair was cytocompatible and promoted mineralized nodule deposition in 21 days and cell migration in 3 days. In conclusion, Bio-C Repair had adequate radiopacity above 3mm Al, solubility less than 3%, dimensional expansion, and low volumetric change. In addition, Bio-C Repair promoted an alkaline pH and presented bioactivity and biocompatibility similar to MTA and Biodentine, showing potential for use as a repair material.

Physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic repair material

Abstract The aim of this study was to evaluate the physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic material, Bio-C Repair (Angelus), in comparison with White MTA (Angelus) and Biodentine (Septodont). The physicochemical properties of setting time, radiopacity, pH, solubility, dimensional and volumetric changes were evaluated. Biocompatibility and bioactivity were assessed in Saos-2 osteoblast cell cultures by the MTT assay 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), Alizarin Red (ARS), and cell migration tests. Statistical analysis was performed by ANOVA, Tukey or Bonferroni tests (α = 0.05). Bio-C Repair had the longest setting time (p < 0.05), but radiopacity and solubility were accordance with the ISO 6876/2012 standards, besides linear expansion. Bio-C Repair and MTA had similar volumetric change (p > 0.05); lower than Biodentine (p < 0.05). All the materials evaluated had an alkaline pH. Bio-C Repair was cytocompatible and promoted mineralized nodule deposition in 21 days and cell migration in 3 days. In conclusion, Bio-C Repair had adequate radiopacity above 3mm Al, solubility less than 3%, dimensional expansion, and low volumetric change. In addition, Bio-C Repair promoted an alkaline pH and presented bioactivity and biocompatibility similar to MTA and Biodentine, showing potential for use as a repair material.

Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas, citotoxicidade e bioatividade de um novo material biocerâmico pronto para uso, Bio-C Repair (Angelus), em comparação com MTA Branco (Angelus) e Biodentine (Septodont). Foram avaliadas as propriedades físico-químicas de tempo de presa, radiopacidade, pH, solubilidade, alterações dimensionais e volumétricas. A biocompatibilidade, bioatividade e capacidade de reparo foram avaliadas em culturas de células de osteoblastos Saos-2 pelo ensaio MTT brometo de 3-(4,5-dimetiltiazol-2-il)-2,5-difeniltetrazólio), vermelho neutro (NR), vermelho de alizarina ( ARS) e testes de migração celular. A análise estatística foi realizada pelos testes ANOVA, Tukey ou Bonferroni (α = 0,05). Bio-C Repair apresentou o maior tempo de presa (p < 0,05), mas radiopacidade e solubilidade de acordo com as normas ISO 6876/2012, além de expansão linear. Bio-C Repair e MTA tiveram variação volumétrica semelhante (p > 0,05), menor que Biodentine (p < 0,05). Todos os materiais avaliados apresentaram pH alcalino. Bio-C Repair foi citocompatível, além de promover deposição de nódulos mineralizados em 21 dias e migração celular em 3 dias. Em conclusão, o Bio-C Repair apresentou radiopacidade adequada acima de 3mmAl, solubilidade menor que 3%, expansão dimensional e baixa perda volumétrica.. Além disso, o Bio-C Repair promoveu um pH alcalino e apresentou bioatividade e biocompatibilidade semelhantes ao MTA e Biodentine, mostrando potencial para uso como material reparador

Biocompatibility and bioactive potential of an experimental tricalcium silicate-based cement in comparison with Bio-C repair and MTA Repair HP materials.

AIM: To evaluate the tissue reaction of a tricalcium silicate-based repair material associated with 30% calcium tungstate (TCS + CaWO4 ) in comparison to Bio-C Repair (Bio-C; Angelus) and to MTA Repair HP (MTA HP; Angelus). METHODOLOGY: Polyethylene tubes filled with one of the materials or left empty (control group, CG) were implanted into the subcutaneous tissues of rats for 7, 15, 30 and 60 days (n = 32/group). The capsule thickness, number of inflammatory cells, collagen content, interleukin-6 (IL-6), osteocalcin (OCN), von Kossa reaction and analysis under polarized light were evaluated. The data were subjected to generalized linear models for repeated measures, except the OCN. OCN data were submitted to Kruskal-Wallis and Dunn's post hoc test and Friedman followed by Nemenyi's test at significance level of 5%. RESULTS: At all time points, significant differences in the number of inflammatory cells were not observed between TCS + CaWO4 and Bio-C, whereas, at 15, 30 and 60 days, no significant difference was detected between TCS + CaWO4 and MTA HP. At all periods, significant differences were not detected in the number of fibroblasts in TCS + CaWO4 versus MTA HP, and, at 60 days, no significant difference was demonstrated between these groups and CG. Significant differences in the immunoexpression of IL-6 were not detected amongst bioceramic materials at all periods. From 7 to 60 days, significant reduction in the number of inflammatory cells, number of IL-6-immunopositive cells and in the capsule thickness was accompanied by significant increase in the collagen in all groups. OCN-immunolabelled cells, von Kossa-positive structures and amorphous calcite deposits were observed around all materials, whereas, in the CG, these structures were not seen. CONCLUSIONS: These findings indicate that the experimental material (TCS + CaWO4 ) is biocompatible and has a bioactive potential, similar to the MTA HP and Bio-C Repair, and suggest its use as a root repair material.

Participation of fibroblast growth factor-1 and interleukin-10 in connective tissue repair following subcutaneous implantation of bioceramic materials in rats.

AIM: To evaluate whether the bioceramic materials Bio-C Pulpo (Bio-C, Angelus) and mineral trioxide aggregate (MTA) Repair HP (MTA-HP, Angelus) induce fibroblast proliferation and release of interleukin-10 (IL-10), an anti-inflammatory cytokine, stimulating connective tissue remodelling. The tissue response of Bio-C and MTA-HP was compared with the White MTA (WMTA; Angelus) since studies have demonstrated that WMTA induces tissue repair. METHODOLOGY: Bio-C, MTA-HP and WMTA were inserted into polyethylene tubes and implanted in the subcutaneous tissue of Holtzman rats for 7, 15, 30 and 60 days. As a control group (CG), empty tubes were implanted subcutaneously. The number of fibroblasts (FB), Ki-67-, fibroblast growth factor-1- (FGF-1) and IL-10-immunolabelled cells and collagen content in the capsules was obtained. The data were subjected to two-way anova followed by Tukey's test (p ≤ .05). RESULTS: At 7 days, significant differences in the number of FB were not detected amongst Bio-C, MTA-HP and WMTA groups (p Ëƒ .05). The capsules of all groups exhibited a significant increase in the number of FB and content of collagen over time. From 7 to 60 days, a significant reduction in the number of FGF-1- and Ki-67-immunolabelled cells was seen in the capsules of all specimens. In all periods, no significant difference in the number of FGF-1-immunolabelled cells was detected between Bio-C and CG specimens. At 60 days, significant differences in the immunoexpression of FGF-1 were not observed amongst the groups. At 7 and 15 days, the highest immunoexpression for Ki-67 was present in Bio-C specimens whilst, after 30 and 60 days, no significant difference was observed amongst the bioceramic materials. At 7 days, few IL-10 immunolabelled cells were present in the capsules of all specimens whereas, at 60 days, a significant increase in the IL-10-immunostaining was present in all groups. At 60 days, the Bio-C, MTA-HP and WMTA groups showed a greater number of IL-10-immunolabelled cells than in the CG specimens (p < .0001). CONCLUSIONS: Bio-C, MTA-HP and WMTA stimulate fibroblast proliferation, leading to the formation of collagen-rich capsules. FGF-1 and IL-10 may mediate the remodelling of capsules around Bio-C, MTA-HP and WMTA bioceramic materials.

Diamond-coated ultrasonic tip decreases debris and uninstrumented surface after preparation of curved canals with isthmus

Abstract The aim of this study was to evaluate root canal preparation with nickel titanium rotary instruments and complementary preparation with ultrasonic tip in curved canals of mandibular molars with isthmus. Twenty-eight mesial roots of mandibular molars with curvature between 20° and 40° and presence of isthmus throughout the entire extension of the root canals were prepared using ProDesign Logic CM (PDL) up to size 40.05, or HyFlex EDM (HFEDM) up to size 40.04. Complementary preparation was performed in the isthmus region using the ultrasonic insert E18D (Helse, Istmo Diamantada). The root canals were scanned using micro-CT (SkyScan 1176) at 9 µm voxel size before and after each preparation step. Transportation, percentage of increase in volume, debris and uninstrumented surface (UNS) were evaluated. Mann Whitney, Wilcoxon, paired and non-paired t-tests were used for statistical analysis (α = 0.05). The canals prepared with PDL and HFEDM obtained similar results for all the variables assessed before using E18D (p > 0.05). E18D significantly decreased the percentage of debris and UNS values in both Groups (p < 0.05). The complementary preparations with E18D caused a smaller quantity of debris in the isthmus of the canals previously prepared with PDL in comparison with HFEDM (p < 0.05). PDL and HFEDM provided similar root canal preparation. PDL promoted a smaller quantity of Debris in the isthmus than HFEDM after using E18D. E18D significantly improved cleaning, and reduced Debris and UNS.

Cytotoxicity and bioactive potential of new root repair materials for use with BMP-2 transfected human osteoblast cells.

Modified formulations of calcium silicate repair materials with additives have been developed to enhance handling, consistency, biocompatibility and bioactivity. Considering the relevance of osteoblastic cell response to mineralized tissue repair, human osteoblastic cells (Saos-2 cells overexpressing BMP-2) were exposed to mineral trioxide aggregate (MTA) (with calcium tungstate - CaWO4), MTA HP Repair, Bio-C Repair and Bio-C Pulpo. Cell viability was assessed by 3-(4,5-dimethylthiazol)-2,5-diphenyltetrazolium bromide (MTT) and neutral red (NR), and cell death, by flow cytometry. Gene expression of bone morphogenetic protein 2 (BMP-2), runt-related transcription factor 2 (RUNX-2), and alkaline phosphatase (ALP) osteogenic markers were evaluated by real-time polymerase chain reaction (RT-qPCR). ALP activity and alizarin red staining (ARS) were used to detect mineralization nodule deposition. Bioactive cements presented no cytotoxic effect, and did not induce apoptosis at the higher dilution (1:12). MTA, Bio-C Repair and Bio-C Pulpo exhibited higher ALP activity than the control group (P < 0.05) after 7 days. MTA, MTA HP and Bio-C Pulpo affected the formation of mineralized nodules (p < 0.05). Exposure to all cement extracts for 1 day increased BMP-2 gene expression. RUNX-2 mRNA was greater in MTA, MTA HP and Bio-C Repair. MTA, MTA HP and Bio-C Pulpo increased the ALP mRNA expression, compared with BMP-2 unexposed cells (P < 0.05). Calcium silicate cements showed osteogenic potential and biocompatibility in Saos-2 cells transfected BMP-2, and increased the mRNA expression of BMP-2, RUNX-2, and ALP osteogenic markers in the BMP-2 transfected system, thereby promoting a cellular response to undertake the mineralized tissue repair.

Bioactive potential of Bio-C Pulpo is evidenced by presence of birefringent calcite and osteocalcin immunoexpression in the rat subcutaneous tissue.

As the biocompatibility and bioactive potential of repair materials are desired characteristics in dentistry, the tissue response of Bio-C Pulpo, a bioceramic material launched on the marked by Angelus (Brazil), was compared with Biodentine (Septodont, France) and White MTA (WMTA; Angelus, Brazil). In 32 rats, 148 polyethylene tubes filled with Bio-C Pulpo, Biodentine or WMTA, and empty (CG, control group) were implanted into subcutaneous tissues for 7, 15, 30, and 60 days. The capsule thickness, numerical density of inflammatory cells (IC) and fibroblasts (Fb), amount of collagen, immunohistochemistry detection of interleukin-6 (IL-6) and osteocalcin (OCN), von Kossa and analysis under polarized light were performed. Data were subjected to two-way ANOVA followed by Tukey's test (p ≤ 0.05). At 7 and 15 days, the capsules around Bio-C Pulpo were thicker than in WMTA while, at 30 and 60 days, significant differences were not observed among the groups. Although at 7, 15, and 30 days, a greater number of IL-6-immunostained cells was found in Bio-C Pulpo and Biodentine than in WMTA, no significant difference was detected among the groups at 60 days. In all groups, the number of Fb and collagen content increased significantly over time. The capsules around materials exhibited von Kossa-positive and birefringent structures, and OCN-immunostained cells whereas, in the CG, these structures were not observed. Bio-C Pulpo, similarly to Biodentine and WMTA, is biocompatible, allows the connective tissue repair and presents bioactive potential in connective tissue of rats.

Physicochemical Properties and Antibiofilm Activity of Tricalcium Silicate Cement and its Association with Cetrimide / Propiedades físico-químicas y actividad antibiofilm del cemento de silicato tricálcico y su asociación con cetrimida

Abstract Cetrimide (CTR) is a cationic surfactant detergent with antimicrobial and antibiofilm activity. The aim of this study was to evaluate setting time, pH, solubility and antibiofilm activity of tricalcium silicate cement (TSC) with zirconium oxide (ZrO2) and its association with 0.2 and 0.4% cetrimide. Initial and final setting times (IST and FST) were assessed based on ISO-6876. pH was evaluated at periods of 1,3,7,14 and 21 days. Solubility was analyzed by weight loss. A modified direct contact test (MDCT) on the biofilm of Enterococcus faecalis formed on bovine root dentin blocks was performed, after 6 hours of manipulation and 15 hours of contact time. The analysis was performed by UFC mL ¯¹ counting. The data were analyzed by ANOVA and Tukey's tests (α=0.05). Higher IST was observed for TSC/ZrO2+CTR in both concentrations than for TSC/ZrO2 and lower FST for TSC/ZrO2+0.4% CTR (p0.05). All materials exhibited increased mass. TSC/ZrO2+CTR 0.4% had lower mass gain than the other materials (p<0.05). The highest antibiofilm activity was observed for TSC/ZrO2+CTR in both concentrations, when compared with the positive control (p<0.05). In conclusion, CTR exhibited potential to promote greater antibiofilm activity to tricalcium silicate cement, without harming its physicochemical properties of setting time, pH and solubility.

Resumen Cetrimida (CTR) es un detergente y surfactante catiónico con actividad antimicrobiana y antibiofilm. El objetivo de este estudio fue evaluar el tiempo de fraguado, pH, solubilidad y actividad antibiofilm del cemento de silicato tricálcico (CST) con óxido de zirconio (ZrO2) y su asociación con CTR a 0.2% y 0.4%. Tiempo de fraguado inicial y final (TFI y TFF) fueron determinados con base en las normas ISO-6876. pH fue evaluado en los períodos de 1,3, 7,14 y 21 días. Solubilidad fue analizada por la pérdida de masa/peso. El test de contacto directo modificado (TCDM) fue realizado sobre biofilm de Enterococcus faecalis formado en dentina radicular bovina, después de 6 horas de manipulación de los cementos y 15 horas de contacto. El análisis fue realizado por la cuantificación de UFC mL¯¹. Los datos fueron analizados usando las pruebas de ANOVA y Tukey (α=0.05). Mayor TFI fue observado para CST/ ZrO2+CTR en las dos concentraciones que para TSC/ZrO2 y menor TFF para TSC/ ZrO2+CTR 0.4% (p0.05). Todos los materiales mostraron aumento de masa. TSC/ZrO2+CTR 0.4% tuvo menor gano de masa que los otros materiales (p<0.05). Mayor actividad antibiofilm fue observado para CST/ZrO2+CTR en las dos concentraciones, cuando comparados con el grupo control positivo (p<0.05). En conclusión, CTR demostró potencial para promover superior actividad antibiofilm al cemento de silicato tricálcico (CST), sin perjudicar sus propiedades físico-químicas de tiempo de fraguado, pH y solubilidad.

How do imaging protocols affect the assessment of root-end fillings?

Objectives: This study investigated the impact of micro-computed tomography (micro-CT)-based voxel size on the analysis of material/dentin interface voids and thickness of different endodontic cements. Materials and Methods: Following root-end resection and apical preparation, maxillary premolars were filled with mineral trioxide aggregate (MTA), Biodentine, and intermediate restorative material (IRM) (n = 24). The samples were scanned using micro-CT (SkyScan 1272; Bruker) and the cement/dentin interface and thickness of materials were evaluated at voxel sizes of 5, 10, and 20 µm. Analysis of variance and the Tukey test were conducted, and the degree of agreement between different voxel sizes was evaluated using the Bland and Altman method (p < 0.05). Results: All materials showed an increase in thickness from 5 to 10 and 20 µm (p < 0.05). When evaluating the interface voids, materials were similar at 5 µm (p > 0.05), while at 10 and 20 µm Biodentine showed the lowest percentage of voids (p < 0.05). A decrease in the interface voids was observed for MTA and IRM at 20 µm, while Biodentine showed differences among all voxel sizes (p < 0.05). The Bland-Altman plots for comparisons among voxel sizes showed the largest deviations when comparing images between 5 and 20 µm. Conclusions: Voxel size had an impact on the micro-CT evaluation of thickness and interface voids of endodontic materials. All cements exhibited an increase in thickness and a decrease in the void percentage as the voxel size increased, especially when evaluating images at 20 µm.